- The Sensitization and Its Effect on the Susceptibility of Stainless Steels to Intergranular Stress Corrosion Cracking in Simulated BWR Environment
- ステンレス コウ ノ エイビンカ ト BWR モギ カンキョウチュウ ニ オケ
この論文をさがす
説明
In order to investigate the correlation between the degree of sensitization of stainless steel pipe material and its susceptibility to intergranular stress corrosion cracking (IGSCC) in simulated BWR environment, the following tests were performed on furnace and weld sensitized stainless steel pipes: (1) 10% oxalic acid etch test (JIS G 0571), (2) copper sulfate-sulfuric acid test (JIS G 0575), (3) EPR test, and, (4) CBB test in high temperature pure water. The following conclusions were resulted: (1) The results of the G 0575 test or of the EPR test and the results of the CBB test were in good agreement, (2) Part of specimens that passed the G 0575 test revealed IGSCC in the CBB test, and, (3) Reduction of carbon content of the material below 0.020% immunized the weld HAZ against IGSCC in simulated BWR environment.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 30 (10), 559-564, 1981
社団法人 腐食防食協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206259833088
-
- NII論文ID
- 130004731387
- 130006024549
- 10003063534
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
- http://id.crossref.org/issn/00109355
-
- NDL書誌ID
- 2331335
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可