- A Mechano-Chemical Synthesis of Silver-Ion Conductive Materials in the System Agl-Ag2WO4-Part 2, Vitrification Process by the Ball Milling-
- メカニカルミリングホウ ニ ヨル AgI Ag2WO4ケイギン イオン デンドウセイ ザイリョウ ノ ゴウセイ ソノ 2 ミリング ニ ヨル ヒショウシツカ ハンノウ カテイ
- Part 2, Vitrification Process by the Ball Milling
- その2.ミリングによる非晶質化反応過程
この論文をさがす
抄録
Vitrification process induced by a ball milling was investigated for silver-ion-conducting materials in the system AgI-Ag2WO4. The amorphous materials were obtained over the wide composition range of 30 to 70mol%AgI content. The silver-ion conductivities of a ball-milled sample showed the maximum at a milling time at which the sample was composed of an amorphous phase and a-Ag2WO4 crystalline phase. This result suggested that the amorphous phase was containing a large amount of AgI content and the amorphous phase was a high ion conductive phase. The maximum conductivity 4.8×10-2 Scm-1 at 298 K was observed for the 70AgI⋅0Ag2WO4(mol%) sample ball-milled for 20 h. This conductivity was higher than that of the completely amorphous sample with the same composition.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 51 (9), 662-667, 2004
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206307347200
-
- NII論文ID
- 130000831468
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 7110092
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可