Journal sliding bearing tests were performed under non-lubricated and water-lubricated conditions. Journals made of Al2O3 were slid against bushes made of Sialon, ZrO2, Al2O3, and SUS304 stainless steel. The Al2O3/Al2O3 combination exhibited the best performance under these test conditions. The wear amount and friction coefficient under the water-lubricated condition were smaller than those under the non-lubricated condition except for the case of Sialon/Al2O3 combination. The wear of Sialon might be increased under the influence of the hydrate formed on the sliding surface by tribochemical reaction. The wear amount of Al2O3 journal was largest in the case of SUS304/Al2O3 combination, in which the wear mode was micro-chipping. On application of Al2O3 under the water-lubricated condition, wear of Sialon in the case of Al2O3/Sialon combination, stress corrosion wear of ZrO2 in the case of Al2O3/ZrO2 combination, and wear of Al2O3 by micro-chipping in the case of Al2O3/SUS304 combination must be considered.
収録刊行物
-
- 日本機械学会論文集C編
-
日本機械学会論文集C編 63 (614), 3600-3605, 1997
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206327750016
-
- NII論文ID
- 130004232457
- 110002385298
-
- NII書誌ID
- AN00187463
-
- COI
- 1:CAS:528:DyaK2sXnvV2qu70%3D
-
- ISSN
- 18848354
- 03875024
-
- NDL書誌ID
- 4323438
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可