アルミニウム連続鋳造用０．５５％Ｃ‐１．１％Ｃｒ‐０．５％Ｍｏロール鋼の耐熱き裂性に及ぼす熱処理の影響

DOI Web Site

書誌事項

タイトル別名
  • Effect of heat treatment on resistance to thermal cracking of 0.55%C-1.1%Cr-0.5%Mo roll steel for continuous casting of aluminum.
  • アルミニウム レンゾク チュウゾウヨウ 0.55パーセント C 1.1パーセン

この論文をさがす

説明

Abnormally large thermal cracks were accidentally observed on surfaces of rolls by continuous casting of aluminum. Effects of quenching and tempering condition on resistance to heat checking and high temperature strength of an alloy roll steel was investigated to settle the problem. When an austenitizing temperature is kept constant, the largest resistance to heat checking of the roll steel is obtained in a tempering temperature range between 450°C and 550°C. The resistance to heat checking and the high temperature strength increases with increasing austenitizing temperature.

収録刊行物

  • 軽金属

    軽金属 43 (3), 165-170, 1993

    一般社団法人 軽金属学会

キーワード