- Effect of heat treatment on resistance to thermal cracking of 0.55%C-1.1%Cr-0.5%Mo roll steel for continuous casting of aluminum.
- アルミニウム レンゾク チュウゾウヨウ 0.55パーセント C 1.1パーセン
この論文をさがす
説明
Abnormally large thermal cracks were accidentally observed on surfaces of rolls by continuous casting of aluminum. Effects of quenching and tempering condition on resistance to heat checking and high temperature strength of an alloy roll steel was investigated to settle the problem. When an austenitizing temperature is kept constant, the largest resistance to heat checking of the roll steel is obtained in a tempering temperature range between 450°C and 550°C. The resistance to heat checking and the high temperature strength increases with increasing austenitizing temperature.
収録刊行物
-
- 軽金属
-
軽金属 43 (3), 165-170, 1993
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206338290304
-
- NII論文ID
- 130004209290
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 3812023
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可