Ａｌ‐Ｃｕ‐Ｓｎ合金の粒界近接部におけるθ′相の析出

DOI Web Site

書誌事項

タイトル別名
  • Preciptitation of θ' phase adjacent to grain boundary in Al-Cu-Sn alloys
  • Al Cu Sn ゴウキン ノ リュウカイ キンセツブ ニ オケル シータ ソ

この論文をさがす

説明

The region (D (θ') region) where finer θ' precipitates were formed densely was found adjacent to the grain boundary in Al-(24)wt%Cu-Sn alloys, when solution-treated, quenched and aged at 200250°Ç. In this report, the formation of the D (θ') region in Al-Cu-Sn alloys was studied in relation to quenching conditions and solution-treatment temperatures (Ts) by using a transmission electron microscope. The results obtained are as follows.<br>(1) The D (θ') region was found to be caused by appearance of the region where Sn rich phases precipitated densely in the early stage of aging.<br>(2) The D (θ') region formed only under the condition of fast quenching (i. e. quenching into iced water). The width of D (θ') region and the distance from the grain boundary to D (θ') region increased with lowering Ts.<br>(3) These results would be explained from the following assumption: A transient peak of vacancy concentration profile developes adjacent to the grain boundary in the early stage of aging, owing to the formation of secondary defects inside the grain.

収録刊行物

  • 軽金属

    軽金属 26 (9), 427-431, 1976

    一般社団法人 軽金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ