- Measurement of Young’s Modulus of Titanium-Silver-Iron Alloys. (Studies on the Titanium-Silver-Iron Alloys, 1st Report)
- Ti-Ag-Fe ゴウキン ノ ヤングリツ ニ ツイテ
- Measurement of Young’s Modulus of Titanium-Silver-Iron Alloys. (Studies on the Titanium-Silver-Iron Alloys, 1st Report)
この論文をさがす
抄録
The Young’s modulus and its change accompanied by heat treatment was measured for titanium-silver and titanium-silver-iron alloys by a static method. The Young’s modulus of commercially pure titanium was 10,700 kg/mm2 and this value decreased about 5∼10% with the addition of silver. The Young’s modulus of titanium-silver-0.5% iron alloys containing 5%, 8% and 10% of silver were considerably lower than the values of the same alloys containing 1% and none of silver. But those of titanium-silver-2% iron and titanium-silver-4% iron alloys showed no appreciable change by different silver content. The Young’s modulus of the water-quenched specimens were about 5∼20% lower than those of fully annealed specimens and the difference between the values of the two kinds of specimens was rather greater in the alloys containing iron than in titanium-silver binary alloys. But the Young’s modulus of beta-solid solution was nearly the same as those of slowly cooled structure. No appreciable effect of cold-rolling and subsequent annealing on the Young’s modulus of the titanium-silver-iron alloys was observed in this study.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (1), 1-4, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481526656
-
- NII論文ID
- 130007333001
- 40018257528
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152968
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可