銅における立方体集合組織の成因について

DOI Web Site Web Site

書誌事項

タイトル別名
  • The Origin of Cribe Texture in Copper
  • ドウ ニ オケル リッポウタイ シュウゴウ ソシキ ノ セイイン ニ ツイテ

この論文をさがす

抄録

In order to test the oriented growth and the oriented nucleation theories of the origin of the cube texture, the orientation relationship between the rolling texture and the annealing texture of a tough-pitch copper strip was examined after secondary rolling at right angle to the primary rolling direction. At low secondary reduction, while shifting of the main component of the rolling texture was hardly abserved, the pole figure for the annealing texture showed that the (200) maxima in the secondary rolling direction were much decreased in intensity and the cube texture might be accounted for by spread from the (001) [100] orientation corresponding to the rotation around the [100] axis parallel to the primary rolling direction. At high secondary reduction, though the main component of the rolling texture was deviated considerably from the (2911) [\bar9\bar45] orientation, the pole figure for the annealing texture was composed mainly of the fairly sharp cube orientation. Such behavior will be difficult to explain in the terms of the oriented growth theory at least.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 25 (2), 151-155, 1961

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ