- タイトル別名
-
- Effect of Iron and Chromium Additions on the Properties of New High Magnetic Permeability Alloys “Nimalloy” in the Nickel and Manganese System
- Ni-Mnケイ シン コウトウジリツ ゴウキン Nimalloy ノ トクセイ ニ オヨボス Fe オヨビ Cr テンカ ノ エイキョウ ニ ツイテ
- Effect of Iron and Chromium Additions on the Properties of New High Magnetic Permeability Alloys “Nimalloy” in the Nickel and Manganese System
この論文をさがす
抄録
Since the original discovery of “Nimalloy” on the Ni-Mn alloys containing about 24%Mn or less which show high permeability when rendered into an optimum degree of order by proper heat treatment. Much work has since been done so as to investigate the effects of various element additions on the properties of Ni-Mn alloys, and numerous alloys having superior magnetic properties have been obtained. It has been known that the cooling rate should be as large as possible for the Ni-Mn-Fe alloys and as small as possible for the Ni-Mn-Cr alloys in order to develop their excellent magnetic properties. Therefore the present authors have investigated the Ni-Mn-Fe-Cr system to obtain the alloys which exhibit the superior magnetic property at a moderate cooling speed as the furnace cooling. As a result, the highest initial permeability of 53950 was obtained on the alloy composed of 78.59%Ni, 14.01%Mn, 4.05%Fe and 3.35%Cr when cooled at a rate of 240°C/hr from 900°C, and the highest maximum permeability of 231000 on the alloy of 78.64%Ni, 14.46%Mn, 4.02%Fe and 2.88%Cr when cooled at a rate of 100°C/hr from 900°C. The latter alloy shows a coercive force of 0.0043 Oe and a magnetic hysteresis loss of 11.42 erg/cm3/cycle for a maximum magnetic induction of 2000G, its electrical resistivity being 75.0 μΩ-cm at 20°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 34 (12), 1237-1242, 1970
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206485956864
-
- NII論文ID
- 130007339936
- 40018256901
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8372215
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可