The logarithmic decrement δ and the rigidity modulus G were investigated for heat-treated and cold-worked Al-Ge alloys containing 2 to 20 mass%Ge. The δ and G values were measured by an inverted torsion pendulum method.<BR>The δ values upon furnace cooling were somewhat higher than those upon water quenching, which were as low as 0.007. By cold working after heat treatment, the δ values of all alloys were increased considerably. With increasing Ge concentration, the δ upon cold working increased abruptly to 5 mass%Ge and then increased gradually. Moreover, in alloys cold worked after furnace cooling, the δ became higher than those cold-worked after water quenching.<BR>With increasing Ge concentration, the G increased, and cold working after heat treatment caused G to decrease. The ΔG effect increased abruptly up to 5 mass%Ge and then increased gradually, and high δ values were obtained in the alloys with a large ΔG effect.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 55 (5), 601-604, 1991
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206486096000
-
- NII論文ID
- 130007340178
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3720957
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可