Grain Size Distribution at the Bottom Region in Very Narrow Cu Interconnects
-
- INAMI Takashi
- Faculty of Engineering, Ibaraki University
-
- TAMAHASHI Kunihiro
- Faculty of Engineering, Ibaraki University
-
- NAMEKAWA Takashi
- Faculty of Engineering, Ibaraki University
-
- CHIBA Akio
- Faculty of Engineering, Ibaraki University
-
- ONUKI Jin
- Faculty of Engineering, Ibaraki University
この論文をさがす
説明
Crystal grain sizes less than 40 nm diameter, i.e., mean free path of an electron in Cu, in both the upper and bottom part of Cu interconnects with 70 nm width and 150 nm depth as a function of overburden Cu plated films with 150 nm, 300 nm and 450 nm thickness have been evaluated by X-ray diffraction method. In the upper part of the Cu interconnects, the frequency ratio of the crystal grains with less than 40 nm diameter was quite small and changed little in the Cu interconnects among overburden Cu films with different thickness. In the bottom part of the Cu interconnect, however, the frequency ratio of the crystal grain with less than 40 nm diameter was found to be very dependent on the thickness of overburden Cu films. The frequency ratio was about 20% at the overburden Cu film thickness of 150 nm, while the frequency ratio decreased to less than 2% at the overburden Cu film thickness of 450 nm. The resistivity of narrow Cu interconnects was found to increase with the increase of the frequency ratio of crystal grains less than 40 nm diameter at the bottom part of Cu interconnects.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 84 (3), 151-155, 2016
公益社団法人 電気化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206499874816
-
- NII論文ID
- 130005131412
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 027144067
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用可