- Properties of Mold Materials Bonded with Aluminum Phosphate and Phosphoric Acid
- リン酸アルミニウムとりん酸を粘結材とする鋳型材の性質
- リンサン アルミニウム ト リンサン オ ネンケツザイ ト スル イガタザイ
この論文をさがす
説明
Silicious molds using aluminum phosphate (AlPO4) and phosphoric acid (H3PO4) as a binder are heat resistant and acid-decomposeable. The silica sand mold resists up to 1,200°C when the molecular ratio of the binder Al2O3/P2O5 is 0.636, and up to 800°C when Al2O3/P2O5 is 0.304. The zircon sand mold resists up to 1,400°C when Al2O3/P2O5 is 0.636. The binder separates Al2O3⋅mH3⋅PO4nH2O which subsequently loses water during drying, produces a viscous solution and forms a mixture of Al(PO3)3 and AlPO4 at 800°C. When the Al2O3/P2O5 ratio of the binder is higher, silica sand particles bind with acid-soluble AlPO4 preventing sintering of the particles during casting. This mold decomposes readily by dipping into a dilute sulphuric acid solution.
収録刊行物
-
- 鋳物
-
鋳物 53 (4), 181-186, 1981
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206508459392
-
- NII論文ID
- 130004789473
-
- NII書誌ID
- AN00016813
-
- ISSN
- 21860335
- 00214396
-
- NDL書誌ID
- 2310695
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可