- Viscoelastic Properties of Bismaleimide·Triazine Resin
- ビスマレイミド トリアジン ジュシ ノ ドウテキ ネンダンセイ
この論文をさがす
抄録
Dynamic viscoelastic properties were measured on the cured bismaleimide·triazine resins prepared from bis (4-maleimidophenyl) methane as a bismaleimide component and 2, 2-bis (cyanatophenyl) propane as a cyanate component. The compositions of the components were varied from 100/0 to 0/100 in weight percent. The glass transition temperature (Tg) increased with increasing amount of the bismaleimide component, from about 250 to about 340°C. Dependence of Tg on the amount of the bismaleimide component was remarkable especially at the bismaleimide content larger than 50 mol %.
収録刊行物
-
- 高分子論文集
-
高分子論文集 41 (10), 635-641, 1984
公益社団法人 高分子学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206522586752
-
- NII論文ID
- 130003836917
-
- NII書誌ID
- AN00085011
-
- ISSN
- 18815685
- 03862186
-
- NDL書誌ID
- 3008160
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可