ゾーン延伸法により作製した高弾性率，高強度ポリエチレン繊維の力学的性質と繊維構造

DOI Web Site

書誌事項

タイトル別名
  • Relationship between mechanical properties and fiber structure for zone-drawn polyethylene fibers.
  • ゾーン エンシンホウ ニ ヨリ サクセイシタ コウ ダンセイリツ コウ キョウ

この論文をさがす

説明

Mechanical properties of highly drawn polyethylene fibers produced by a continuous zone-drawing method were studied and related to fiber structure. Young's modulus and tenacity increased linearly with an increase in the drawing stress and also showed a good linear relationship with the amorphous birefringence. The stress-optical coefficient in amorphous phase depended strongly on the drawing temperature; it's value was 0.5 GPa-1 for the fibers drawn at the temperature above 115°C. Linkages of the crystalline blocks will be formed at degrees of crystallinity beyond 77%, and this results in the high Young's modulus. Tenacity was mainly dependent on the degree of crystallinity.