Ｓｉ表面におけるＴｉＳｉ２の膜の成長と酸化

DOI Web Site オープンアクセス

書誌事項

タイトル別名
  • Growth and oxidation of TiSi2 film on Si surface.
  • Si ヒョウメン ニ オケル TiSi2 ノ マク ノ セイチョウ ト サンカ

この論文をさがす

説明

We found that the mean grain size of TiSi2 films on Si wafers deponds on deposited Ti amount of every time rather than annealing temperature. From SEM micrographs, it was found that no morphologies are varied before and after oxidation in air at temperature from 100°C to 800°C. But above 1000°C, the TiSi2 film was thermally grooved at its grain boundaries and grain size was increased. From analytic electron microscope photographs, it was found that crystalline grain represent TiSi2, but the grain boundary was found to be Ti free-zone.<BR>Quantitative depth profile of chemical composition of the thermal oxide of the TiSi2 have been studied by XPS in conjunction with argon ion sputtering. From chemical depth profiles of the thermal oxide of TiSi2, we observed that SiO2 is dominant in oxide products of the TiSi2 at various oxidation temperatures. From FWHM and Si/Ti atomic ratio analysis, we can see that except for the TiO2, TiOx was detected, but no the intermediate Ti-silicide (TiSi and Ti5Si3) in oxidized TiSi2. We also observed the growth of a Ti-free layer of SiO2 at 1000°C.

収録刊行物

  • 真空

    真空 28 (1), 30-41, 1985

    一般社団法人 日本真空学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ