Electrodeposition of Al<sub>2</sub>O<sub>3</sub> Composite Cr-C Alloy Coatings from Oxalic Bath
-
- MORIKAWA Tsutomu
- Technology Research Institute of Osaka Prefecture
-
- NAKADE Takuo
- Technology Research Institute of Osaka Prefecture
Bibliographic Information
- Other Title
-
- シュウ酸浴からのAl<sub>2</sub>O<sub>3</sub>複合Cr-C合金めっき
- シュウ酸浴からのAl₂O₃複合Cr-C合金めっき
- シュウサンヨク カラ ノ Al ₂ O ₃ フクゴウ Cr-C ゴウキンメッキ
Search this article
Abstract
<p>Electrodeposited Al2O3 composite Cr-C alloy coatings were produced from an oxalic acid bath prepared by adding oxalic acid to a hot CrO3 solution. Chromium ions in the oxalic bath include Cr3+ oxalate complex and Cr6+ ions. The Al2O3 particles were co-deposited easily along with the Cr-C alloy coating from the oxalic bath. The content was controlled up to about 3 wt% by plating conditions. The Al2O3 contents of the coatings decreased with current density and increased with bath temperature. The added amount of oxalic acid at make-up of the bath increased the Al2O3 contents of the coatings. The co-deposition mechanism was supported with a two-step adsorption mechanism proposed by Guglielmi, but the adsorption of Al2O3 tothe cathode in the oxalic bath was much weaker than that of either Ni composite plating or Cr composite plating.</p>
Journal
-
- Journal of The Surface Finishing Society of Japan
-
Journal of The Surface Finishing Society of Japan 67 (12), 685-688, 2016
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679095017856
-
- NII Article ID
- 130006236567
- 40021028111
-
- NII Book ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL BIB ID
- 027784839
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed