The microstructure and wear properties of laser-clad WC-Cr3C2 cermet coating on steel substrate
-
- Wu Qianlin
- Institute of Marine Materials Science and Engineering, Shanghai Maritime University
-
- Li Wenge
- College of Materials Engineering, Shanghai University of Engineering Science
書誌事項
- タイトル別名
-
- The Microstructure and Wear Properties of Laser-Clad WC-Cr<SUB>3</SUB>C<SUB>2</SUB> Cermet Coating on Steel Substrate
この論文をさがす
抄録
WC-Cr3C2 cermet coating on carbon steel was fabricated by laser controlled reactive synthesis and exhibited the metallurgical bonding at the interface between coating and substrate. The microstructure and wear properties of laser-clad WC-Cr3C2 Cermet Coating on steel substrate have been investaged by means of scaning eletron microscopy (SEM), X-ray diffraction (XRD), microhardness testing and wear testing. Experimental results show that the coating has a very good thermal resistance and high bonding strength due to Ni addition, which decreases stress concentration at the interface and increases the bonding strength due to better wettability. The coating shows superior hardness and wear resistance. In the same wear conditions, the wear resistance of the coating is 4 times than that of steel substrate.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (3), 560-563, 2011
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227347456
-
- NII論文ID
- 10027839021
- 130004454659
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10990888
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可