- Naiki Masahiro
- Polymer Research Laboratory, Ube Industries, Ltd., Kogushi, Ube
この論文をさがす
抄録
A polyimidepolysiloxane was synthesized from 2,3,3',4'-biphenyltetracarboxylic acid dianhydride, 5,5'-methylene-bis(antranilic acid) and (,(-bis(3-aminopropyl)polydimethylsiloxane. It was used for a heat-curable solder resist having flame retardancy without flame retardant agent such as halogenated compounds. Addition of talc to the composition was effective for increasing flame retardancy. The developed solder resist achieved level 0 in UL94V test in TCP-type layered product. It had excellent flexibility and insulation reliability under a high-temperature and high-humidity environment.
収録刊行物
-
- Journal of Photopolymer Science and Technology
-
Journal of Photopolymer Science and Technology 20 (2), 149-152, 2007
フォトポリマー学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679300795392
-
- NII論文ID
- 130004464516
- 40015602466
-
- NII書誌ID
- AA11576862
-
- COI
- 1:CAS:528:DC%2BD2sXot1Wnt7k%3D
-
- ISSN
- 13496336
- 09149244
-
- NDL書誌ID
- 8918753
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可