絶縁用封止材として使われるエポキシ樹脂硬化反応の解析　第２報　　エポキシ樹脂の粘弾性構成則と界面完全接着モデルによる応力　　ひずみ解析

DOI

書誌事項

タイトル別名
  • Analysis of Curing Reaction for Epoxy Resin Used for Electrical Insulators
  • 第2報 エポキシ樹脂の粘弾性構成則と界面完全接着モデルによる応力-ひずみ解析

この論文をさがす

説明

A kinetic analysis of the curing reaction between an epoxide (Epikote 828) and a carbonic acid anhydride (HN-2200) using a finite element analysis with a coupled matrix has been previously reported. Shrinkage of the epoxy resin during the cure creates an internal stress. Both the reaction rate and the material constitutive relationships have great influence on the internal stress. Although stress relaxation reduces the internal stress, it has not been taken into account in the previous work. In order to introduce the effects of stress relaxation of the epoxy resin in the finite element analysis, the relaxation modulus was obtained from complex modulus measurements made on a dynamic mechanical analyzer. The relaxation modulus was expressed as a Prony series. The influence of stress relaxation on reducing the internal stress of the epoxy resin was estimated with this relaxation modulus. The Maximum equivalent stress after stress relaxation was one-fiftieth that without the stress relaxation. Experimental results showed good agreement with those of numerical analysis without mean normal stress relaxation when the epoxy resin was put between metal parts. This indicated that the mean normal stress relaxation of epoxy resin is negligible.

収録刊行物

  • 成形加工

    成形加工 14 (8), 512-518, 2002

    一般社団法人 プラスチック成形加工学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390282679438729216
  • NII論文ID
    130003691202
  • DOI
    10.4325/seikeikakou.14.512
  • ISSN
    18837417
    09154027
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ