Improved Superconducting Properties of Y123 Melt-solidified Bulks through Controlling Crystal Growth Direction and Cation Stoichiometry

DOI Web Site 16 References

Bibliographic Information

Other Title
  • 結晶成長方位および金属組成制御によるＹ１２３溶融凝固バルクの超伝導特性の改善
  • ケッショウ セイチョウ ホウイ オヨビ キンゾク ソセイ セイギョ ニ ヨル Y123 ヨウユウ ギョウコ バルク ノ チョウデンドウ トクセイ ノ カイゼン

Search this article

Abstract

Two new approaches to fabricate Y123 melt-solidified bulks with excellent superconducting properties have been developed. One is a new method of crystal growth from a seed crystal with its c-axis parallel to the top surface, and the other is a high-temperature annealing process under a moderately reducing atmosphere after crystal growth. In the present study, the former method increased the area of high-Jc regions, and the latter enhanced Jc, particularly at positions far from the seed crystal at low temperatures through suppression of yttrium substitution for barium. The field-trapping property was also improved through introduction of a reductive annealing process prior to oxygen annealing at low temperatures.

Journal

References(16)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top