含クロム炭素飽和溶鉄とBaO-BaF<SUB>2</SUB>系フラックス間のりんの分配平衡および同系フラックス中のBaOの活量

DOI Web Site Web Site 被引用文献1件 参考文献3件

書誌事項

タイトル別名
  • Phosphorus Partition between Fe-Cr-C Melts and BaO-BaF<SUB>2</SUB> Fluxes and the Activity of BaO
  • 含クロム炭素飽和溶鉄とBaO-BaF2系フラックス間のりんの分配平衡および同系フラックス中のBaOの活量
  • ガン クロム タンソ ホウワ ヨウテツ ト BaO BaF2ケイ フラックスカ

この論文をさがす

抄録

The phosphorus partition between BaO-BaF2 fluxes and Fe-Cr-Csatd. alloys was measured at temperatures ranging from 1 175°C to 1 300°C under a CO atmosphere.<BR>The phosphorus partition ratio increases with increasing BaO content in the fluxes and decreases with increasing chromium content in Fe-Cr-Csatd. alloys. The BaO-BaF2 system was found to have a large phosphate capacity ranging from 1026 to 1028.5 at 1300°C, which is much larger than that for the CaO-CaF2 system. The enthalpy change for the dephosphorization reaction by BaO bearing fluxes was determined to be-528 kJ/mol. The chromium partition ratio increases with an increase in BaO content especially in the higher BaO content range. The possibility of the removal of phosphorus from Fe-16% Cr-C alloys without much oxidation loss of chromium by using 50% BaO-50% BaF2 flux was demonstrated.<BR>Furthermore, the activity of BaO for the BaO-BaF2 system was determined at 1 200°C and 1 300°C and the activity of BaF2 was calculated by using the Gibbs-Duhem relationship. The phase diagram for the BaO-BaF2 system was also discussed.

収録刊行物

  • 鉄と鋼

    鉄と鋼 76 (3), 352-359, 1990

    一般社団法人 日本鉄鋼協会