Sterically stabilized liposomes were produced by incorporation a poly (oxyethylene) poly (oxypropylene) block copolymer (Pluronic F-68) into the lipid bilayer using a high-pressure homogenizer. Mean vesicle size of liposomes incorporating Pluronic F-68 greatly decreased from 480 nm to 110 nm with minor change in marker entrapment after passing three times through the high-pressure homogenizer. Liposomes stabilized with Pluronic F-68 were characterized with respect to entrapment efficiency, vesicle size and surface charge. Entrapment efficiency of a marker increased with Pluronic F-68 content, and was maximum at 0.13 (% wt/vol) -Pluronic F-68. In particle size and surface charge, no change was noted with increase in Pluronic F-68 content. Surface charge decreased slightly for liposomes incorporating Pluronic F-68, compared to those coated with Pluronic F-68. Pluronic F-68 is thus distributed between the bilayer and/ or inner phase of liposomes as well as the liposome surface. Liposomes stabilized with Pluronic F-68 were significantly stable in calcium and fetal bovine serum (FBS) solution at 37°C compared with Pluronic F-68-free liposomes. The incorporation of Pluronic F-68 into the bilayer caused significant increase in 31P-NMR line width. Pluronic F-68 is thus shown to stabilize liposomes by restricting phospholipid motion in the bilayer.
収録刊行物
-
- 油化学
-
油化学 43 (7), 567-573, 1994
公益社団法人 日本油化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680311221120
-
- NII論文ID
- 10006946267
-
- NII書誌ID
- AN00245435
-
- ISSN
- 0513398X
- 18842003
-
- NDL書誌ID
- 3893780
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可