果樹皮を原料とするバイオコークスの形成特性～ASEAN諸国との果樹貿易から産出される未利用バイオマス資源の有効活用～
書誌事項
- タイトル別名
-
- Forming Properties of Bio-coke Using Fruit Peels as Raw Material～Effective Utilization of Unused Biomass Resources Obtained from Imported Fruit from ASEAN Countries～
- カジュヒ オ ゲンリョウ ト スル バイオコークス ノ ケイセイ トクセイ : ASEAN ショコク ト ノ カジュ ボウエキ カラ サンシュツ サレル ミリヨウ バイオマス シゲン ノ ユウコウ カツヨウ
この論文をさがす
説明
In recent years, the development of bio-energy in cooperation with an ASEAN country is a very important issue for both participating countries, which would be able to build a win-win relationship. ASEAN countries have a large amount of unused biomass resources. However, raw biomass business does not seem to work well based on experience unless a new technology is introduced. The Bio-coke (referred to as BIC) is a domestic energy technology in Japan. In this study, Bio-coke made from unused resources of fruits that are imported in large quantities from ASEAN countries is being focused. The compressive strength measured for Banana peel Bio-coke was 98.4 MPa at initial moisture of 1.81 mass% while the Orange peel Bio-coke measured 167.0 MPa at initial moisture of 0.52 mass%. Meanwhile, the apparent Yang's modulus ratio based on cool compressive test for the former is about 4.0 GPa and 4.5GPa for the latter. Through hot compressive test at 973 K, 8 MPa was recorded for Banana peel Bio-coke and about 4.2 MPa for Orange peel Bio-coke.
収録刊行物
-
- Journal of Smart Processing
-
Journal of Smart Processing 3 (5), 276-282, 2014-09-20
一般社団法人 スマートプロセス学会 （旧高温学会）
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680392384896
-
- NII論文ID
- 130005091327
-
- NII書誌ID
- AA12553487
-
- ISSN
- 21871337
- 2186702X
-
- NDL書誌ID
- 025825309
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可