Influence of a Photo-Acid Generator on the Photoreactivity of a Photosensitive Polyimide Containing Epoxy Groups.
-
- Yu Han Sung
- Department of Chemistry and Biotechnology, Graduate School of Engineering, The University of Tokyo
-
- Yamashita Takashi
- Department of Chemistry and Biotechnology, Graduate School of Engineering, The University of Tokyo
-
- Horie Kazuyuki
- Department of Chemistry and Biotechnology, Graduate School of Engineering, The University of Tokyo
この論文をさがす
説明
Photochemical reactivity of a polyimide containing epoxy groups, PI(6FDA/ep-AHHFP), was studied in the presence of diphenyl-iodonium 9,10-dimethylanthracene-2-sulfonate (DIAS) as a photo-acid generator. IR spectroscopy was used for measuring the extent of ring-opening polymerization of epoxy groups, which was influenced by photoirradiation and post-cure conditions. By DIAS having an absorption band in 350–410 nm, the irradiation time was shortened by twenty times for getting the same conversion compared to the previous case with diphenyliodonium hexafluoroarsenate (DPI-AsF6). The activation energy for epoxy polymerization of PI(6FDA/ep-AHHFP) with DIAS was about 14 kJ mol−1. The kinetic chain length, v, per one acid in PI(6FDA/ep-AHHFP) with DIAS was calculated to be about 4–31. The reaction radius, rR, of an acid is about 8–16 Å when heated for 5–40 min at 50–195°C, which is about half for DPI-AsF6. The gel dose, D0gel, and contrast, γ, based on incident energy after post-cure at 100°C for 30 min are 117 mJ cm−2 and 4.0, respectively. The quantum yield for crosslinking of PI(6FDA/ep-AHHFP), Φgel, was 0.084 from the characteristic curve. PI(6FDA/ep-AHHFP) containing DIAS works as a negative-tone photosensitive polyimide.
収録刊行物
-
- Polymer Journal
-
Polymer Journal 28 (8), 703-707, 1996
The Society of Polymer Science, Japan
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681267633024
-
- NII論文ID
- 10006268675
-
- NII書誌ID
- AA00777013
-
- COI
- 1:CAS:528:DyaK28Xlt1yksb8%3D
-
- ISSN
- 13490540
- 00323896
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可