- Effect of Li-addition to the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System. (II).
- Bi Pb Sr Ca Cu Oケイ コウオンソウ エ ノ Li テンカ コウ
この論文をさがす
抄録
The effects of Li-addition to the high-Tc phase in Bi-Pb-Sr-Ca-Cu-O system have been studied for the samples with the nominal composition of Bi:Pb:Sr:Ca:(Cu, Li)=0.96:0.24:1.0:1.1:(1.6-x, x) heated at 840 to 845°C for 144h in air (x=0 to 0.2). The characterization of the samples has been made by DTA, the measurements of XRD and DC electrical resistivity, SEM observation and ICP analysis. The Li-addition promotes the formation of the high-Tc phase. The sample with x=0.05 heated at 842°C for 144h exhibits Tc=116K, while Tc=109K for the Li-free sample (x=0) heated at 842°C for 120h. The results of ICP analysis showed that the Li content of the samples heated at 842°C for 120h was very low.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 39 (5), 386-389, 1992
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681281385088
-
- NII論文ID
- 130000818178
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3769703
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可