- Wettability and bonding strength between copper base alloys and sintered Al2O3 compacts.
- Al2O3 ショウケツタイ ニ タイスル ドウ ゴウキン ノ ヌレセイ ト セ
この論文をさがす
説明
Studies on the wettability and the bonding of Cu-Sn-Ti system (pure metals except for Ti, binary alloys and a ternary alloy) against sintered Al2O3 compacts were carried out. Results obtained were as follows:<BR>(1) Wettability of Cu, Sn pure metals, Cu-10%Sn and Cu-5%Ti binary alloys in vacuum (1.3×10-2-4.0×10-3 Pa) were unsatisfactory. On the other hand, Cu-10%Sn-5%Ti ternary alloy was comparatively wettable, where reaction layer corresponding to Ti3Al containing slight Cu and Sn was formed in the interface between brazing alloy and sintered Al2O3 compact. Sn-5%Ti binary alloy against sintered Al2O3 showed fairly excellent wettability, but did not form any reaction layer between them.<BR>(2) Bonding strength of sintered Al2O3 compacts brazed with Cu, Sn pure metals and Cu-10%Sn or Cu-5%Ti binary alloys had a tendency to decrease with increasing the degree of vacuum (or with decreasing oxygen partial pressure) of bonding atmosphere. Bonding strength of sintered Al2O3 compacts brazed with Sn-5%Ti and Cu-l0%Sn-5%Ti alloys which were good wettable to sintered Al2O3 were comparatively high, and those had a tendency to increase with raising bonding temperature.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 35 (6), 543-547, 1988
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681284458880
-
- NII論文ID
- 130000813352
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaL1MXotFSmtA%3D%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3653897
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可