- Change in Structure by Heat Treatment of SUS316L HS-PM Process Material.
- SUS316L タカヒズミ フカ PM プロセスザイ ノ ネツ ショリ ニ ヨル ソシキ ヘンカ
この論文をさがす
説明
The high strain powder metallurgy (HS-PM) process was applied to an SUS316L gas atomized powder by 360ks mechanical milling (MM) with a planetary ball mill under an Ar atmosphere. The MM powder was annealed at 1073 K, 1173 K, 1273 K. Each structure was investigated using XRD and TEM/EDS. It was confirmed that as-MM powder consisted of an ultra fine (α+γ) microduplex structure. It was supposed that the a phase was formed as the HS-PM process by increasing free energy of the austenitic phase. Fine grain structure with its grain size of 2.3μm composed of fine carbides and γ phase was obtained when MM powder was annealed at 1073 K for 3.6 ks. It was also confirmed that these fine carbides restrain the grain growth. But at 1173 K and 1273 K, the fine carbides were not seen, so that grain size increased drastically.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 49 (6), 479-485, 2002
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681286242688
-
- NII論文ID
- 10008833448
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 6190473
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可