- Effect of water cooling conditions on splash break occurance during aluminum DC casting
この論文をさがす
説明
The cooling water used in vertical aluminum DC casting is generally induced to just under the mold to prevent molten aluminum break out. However, the cooling water leaks into the air gap between the mold and the surface of ingot, so water splashes over the top of the molten aluminum, resulting in uneven cooling. But the quantitative survey on the splash break behavior and the change in the cooling condition has not been conducted. Hence, to quantify the splash break condition and the cooling capability, we have made the “Cooling water simulator” capable of freely controlling the potential splash causing factors such as temperature of cooling water, water flow rate, air gap amount, and angle of the water flow, reproducing the splash, and measuring the heat transfer value. The experimental result reveals that the temperature of cooling water is not a factor highly influencing on heat flux and splash, but the splash behavior highly depends on three factors which are the water flow rate, the angle of water flow, and the distance between the cooling water hit point level and the cooling water exit level. And that the heat flux also increases when splash occurs. In addition, the splash break parameter was drawn based on the above three factors, and the correlation between splash break parameter and heat flux was clarified. Use of splash break parameter enables setting of the casting condition where the maximum heat flux is obtained while preventing splash.
収録刊行物
-
- 軽金属
-
軽金属 60 (8), 379-385, 2010
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681316512256
-
- NII論文ID
- 130004482020
-
- ISSN
- 18808018
- 04515994
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可