- The Effect of Age-Hardening on the Rigidity Modulus and the Internal Friction in 17-7PH Stainless-Steel Wire
- 17-7PH フシュウコウセン ノ ジコウ ニ トモナウ ゴウセイリツ , ヒ テイコウ コウド オヨビ ナイブ マサツ ノ ヘンカ ニ ツイテ
この論文をさがす
抄録
The change of the rigidity modulus, the electrical resistivity, the hardness and the internal friction following age-hardening were studied with 17-7PH stainless-steel wire containing 1.24%Al.The measurement were made on specimen of 0.65 mm diameter, using a torsion pendulum, a potentiometer and a micro-Vicker’s hardness tester. The results obtained were as follows: (1) The hardness of 17-7PH stainless-steel wire increased remarkably by aging at 400∼500°, but only slightly by aging at 100∼200°. (2) The electrical resistivity decreased in three temperature ranges of aging, namely, 150∼200°, 300∼450° and 500∼600°. (3) The rigidity modulus increased in the aging temperature range of 100∼250° and 400∼500°, but decreased by aging above 550°. (4) The internal friction of 17-7PH steel wire decreased remarkably by aging at 100∼300°, but increased again by aging at 550∼650°.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 34-36, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459940608
-
- NII論文ID
- 130007335222
- 40018257776
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153216
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可