Ar-SO<SUB>2</SUB>雰囲気中におけるニッケル-クロム合金の高温腐食

DOI Web Site Web Site

書誌事項

タイトル別名
  • High Temperature Corrosion of Ni-Cr Alloys in Ar-SO<SUB>2</SUB> Atmosphere
  • Ar-SO2雰囲気中におけるニッケルークロム合金の高温腐食
  • Ar SO2 フンイキチュウ ニ オケル ニッケル クロム ゴウキン ノ コウ

この論文をさがす

抄録

The simultaneous attack of oxygen and sulphur on a range of Ni-Cr alloys containing 1-20(mass%)Cr has been investigated between 873 and 1173 K in PSO<SUB>2</SUB>=104 Pa atmosphere. Reaction kinetics was traced by using an automatic recording balance, and the scale structures were examined by metallography, scanning electron microscopy and microprobe analysis.<BR>The reaction kinetics was complex and classified into three groups of the temperature ranges. This complexity was owing to the sulphide formation and initial oxide properties. The corrosion kinetics followed more than two-step parabolic rate laws, but not followed by the simple single rate laws. Compared with pure nickel, the addition of up to 13%Cr at 918 K or below and at 1073 K or above, or 20%Cr at 918-1073 K has an effect on corrosion resistance.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ