Effect of Morphology of Grain Boundary Nitride on the Ductility of Fe-30 mass%Cr Alloys
-
- Fukuda Tadashi
- Institute for Materials Research, Tohoku University
Bibliographic Information
- Other Title
-
- Fe-30%Cr合金の延性に及ぼす粒界窒化物の形態の影響
- Fe 30パーセント Cr ゴウキン ノ エンセイ ニ オヨボス リュウカイ チッカブツ ノ ケイタイ ノ エイキョウ
Search this article
Abstract
Effects of morphology of grain boundary nitride on the ductility of Fe-30 mass%Cr alloys containing N from 0.004 to 0.13 mass% were investigated. Two kinds of heat treatments were adopted to obtain the morphologies of continuous grain boundary nitride and of discontinuous grain boundary nitride. Tensile tests were carried out at temperatures ranging from 4.2 K to room temperature. Ductility was evaluated by transition temperatures in reduction of area.<BR>The results obtained are summarized as follows:<BR>(1) Upper shelf in reduction of area of the specimen containing discontinuous grain boundary nitride is higher than that of the specimen containing continuous grain boundary nitride.<BR>(2) Transition temperature of the specimen containing discontinuous grain boundary nitride is lower than that of the specimen containing continuous grain boundary nitride.<BR>(3) The area rate of intergranular fracture surface which appears in cleavage fracture surface observed in the specimen containing discontinuous grain boundary nitride is smaller than that which appears in cleavage fracture surface observed in the specimen containing continuous grain boundary nitride. The area rate of intergranular fracture surface which appears in dimple fracture surface also shows similar observation result.<BR>(4) Initiation of microcracks for brittle fracture may be caused by decohesion at the interfaces between the matrix and grain boundary nitride.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 63 (9), 1137-1140, 1999
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681467196288
-
- NII Article ID
- 10005345834
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214426
-
- NDL BIB ID
- 4859051
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed