書誌事項
- タイトル別名
-
- Prediction of Shrinkage Formation in Investment Castings
- イン ベスト メント チュウゾウヒン ノ シュウシュクス ハッセイ ヨソク
この論文をさがす
抄録
Three-dimentional solidification analysis was performed for investment castings and a method for predicting the shrinkage formation by computing the “F-value”, defined as the sum of solid fraction gradients, was proposed. The calculated F-values for the casting models of a compressor vane, a turbing blade and a impeller with shroud were evaluated with respect to the shrinkage porosity observed in the real castings so as to determine the critical F-value. It was found that the F-values below which the local shrinkage porosity formed were dependent on the alloy composition, e. g., 0.2cm−1 for 17-4PH steels and 13Cr stainless steels, and 0.1cm−1 for vacuum-melted nickel-base superalloys.
収録刊行物
-
- 鋳物
-
鋳物 57 (9), 580-585, 1985
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681483453952
-
- NII論文ID
- 130004789613
-
- NII書誌ID
- AN00016813
-
- ISSN
- 21860335
- 00214396
-
- NDL書誌ID
- 3046023
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可