オゾン酸化法によるγ線重合ポリエチレンの微細構造　Ｉ　　γ線重合ポリエチレンのオゾン酸化物のＧＰＣ分析

DOI Web Site

書誌事項

タイトル別名
  • GPC Analysis of Ozone-Oxidized Polyethylene Prepared by γ-Ray Polymerization in Bulk
  • ガンマセン ジュウゴウ ポリエチレン ノ オゾン サンカブツ ノ GPC ブン

この論文をさがす

抄録

The sample weight is increased largely by ozone-oxidation for polyethylene prepared by γ-rayinduced polymerization in bulk. Two peaks appear in the GPC trace of the oxidized sample, and the ratio of the molecular weights of them is nearly 1: 2. The sample molecular weight decreased by further oxidation for γ-ray-polymerized PE, while the decrease was a little for linear polyethylene single crystals. These results lead to the conclusion that γ-ray-polymerized PE is composed of lamellar crystals with molecular chains folded very irregularly. The molecular weight of the final GPC peak for oxidized samples increases with the increase in polymerization temperature, and corresponds well to the X-ray long period. The dependence of the long periods on polymerization temperature is similar to that of the long period of solution-grown crystals on crystallization temperature. This indicates that the polymers crystallize simultaneously with polymerization by γ-ray. At higher temperatures, however, the polymers formed may crystallize in the cooling process after the polymerization.

収録刊行物

  • 高分子論文集

    高分子論文集 36 (1), 47-53, 1979

    公益社団法人 高分子学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ