低熱膨張型電析Fe-Niインバー合金の形成に及ぼす電解条件の影響

DOI DOI 機関リポジトリ 機関リポジトリ (HANDLE) Web Site ほか2件をすべて表示 一部だけ表示 被引用文献4件 参考文献23件 オープンアクセス

書誌事項

タイトル別名
  • Effects of Electrolysis Conditions on the Formation of Electrodeposited Invar Fe-Ni Alloys with Low Thermal Expansion
  • テイネツ ボウチョウガタデンセキFe-Ni インバー ゴウキン ノ ケイセイ ニ オヨボス デンカイ ジョウケン ノ エイキョウ

この論文をさがす

説明

<p>To elucidate the effects of electrolysis conditions on the formation of electrodeposited invar Fe-Ni alloys with low thermal expansion, Fe-Ni electrodeposition was performed at 10-5000 A·m–2 and 5×105 C·m–2 in agitated solution containing NiSO4, NiCl2, H3BO3, FeSO4, C7H4NNaO3S and C3H4O4 at 40-60°C. Ni content in deposits significantly decreased in the low current density region with increasing current density, reached a minimum, and then increased due to reaching at diffusion limiting current density for Fe deposition as the current density increased further. With increasing the concentration of FeSO4 in solution, Ni content in deposits decreased at lower current density region, reached a constant at lower current density, and then began to increase at higher current density. As a result, the current density range where Ni content in deposits was minimum and constant became wider with higher concentration of FeSO4. With decreasing pH in solution, since the partial polarization curve for H2 evolution and total polarization curve sifted to higher current density region, Ni content in deposits-current density curve shifted to higher current density region. With stirring the solution, Ni content in deposits reached a minimum as the current density increased, and then began to increase at higher current density than without stirring due to increase in diffusion limiting current density for Fe deposition. The change of the composition in deposits by electrolysis condition can be explained by the changes of the total polarization curve for Fe-Ni alloy deposition and the partial polarization curves for Fe and Ni depositions and H2 evolution.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 105 (1), 55-63, 2019

    一般社団法人 日本鉄鋼協会

被引用文献 (4)*注記

もっと見る

参考文献 (23)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ