- 高山 暢久
- Graduate School of Engineering, Kyushu University
-
- 高田 晃彦
- Institute for Materials Chemistry and Engineering, Kyushu University
-
- 小椎尾 謙
- Graduate School of Engineering, Kyushu University Institute for Materials Chemistry and Engineering, Kyushu University WPI-I2CNER, Kyushu University
-
- 高原 淳
- Graduate School of Engineering, Kyushu University Institute for Materials Chemistry and Engineering, Kyushu University WPI-I2CNER, Kyushu University
書誌事項
- タイトル別名
-
- Molecular Aggregation Structure of Notched Nylon 12 Film during Uniaxial Elongation
- ノッチ オ ドウニュウ シタ ナイロン 12 フィルム ノ イチジク シンチョウ カテイ ニ オケル ブンシ ギョウシュウ コウゾウ ヒョウカ
この論文をさがす
抄録
<p>Polarizing observation was carried out for nylon 12 (Ny12) films with a notch of ca. 0.2 mm length during uniaxial elongation. As the result, a ductile deformation behavior was detected, and a X-shaped area with higher retardation was observed around the notch extending to 45˚inclined direction to the uniaxial elongation direction. Moreover, during the uniaxial elongation, in-situ wide angled X-ray diffraction (WAXD) measurement were performed at various positions in the Ny12 film specimens. As a result, a crystal phase transition from γ-crystal to α-crystal seemed to occur in the region where higher retardations were observed. Since the intrinsic birefringence in α-crystal is higher than those in γ-crystal and amorphous phases, the increase in retardation can be caused by increase of α-crystalline fraction.</p>
収録刊行物
-
- 日本ゴム協会誌
-
日本ゴム協会誌 94 (9), 293-298, 2021
一般社団法人 日本ゴム協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390290384176537472
-
- NII論文ID
- 130008128294
-
- NII書誌ID
- AN00269207
-
- ISSN
- 18840442
- 0029022X
-
- NDL書誌ID
- 031677306
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可