Temperature Independences of Fatigue Crack Growth in Ti–0.49 mass%O
-
- Okuyama Yelm
- Department of Control Engineering, National Institute of Technology, Kisarazu College
-
- Tanaka Masaki
- Department of Materials, Kyushu University Center for Elements Strategy Initiative for Structural Materials, Kyoto University
-
- Morikawa Tatsuya
- Department of Materials, Kyushu University
Search this article
Description
<p>The temperature dependence of fatigue crack growth in stage IIb was investigated in Ti–0.49 mass%O with an alpha single phase. It was found that the fatigue crack growth rate in stage IIb was temperature independent at temperatures above 300 K. EBSD maps beside the fatigue crack showed that prismatic slips with 〈a〉 dislocations were dominantly activated during the fatigue crack growth. The reason why the prismatic slips were dominantly activated is discussed with numerical crystal plasticity analysis. It was shown that the local strain rate at the notch tip was higher than the macroscopic strain rate, which leads to the suppression of non-prismatic slips at the fatigue crack tip.</p>
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 63 (4), 600-606, 2022-04-01
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390291767726353792
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 032072003
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- KAKEN
- OpenAIRE
-
- Abstract License Flag
- Disallowed