Temperature Independences of Fatigue Crack Growth in Ti–0.49 mass%O

DOI Web Site Web Site 被引用文献3件 参考文献23件 オープンアクセス
  • Okuyama Yelm
    Department of Control Engineering, National Institute of Technology, Kisarazu College
  • Tanaka Masaki
    Department of Materials, Kyushu University Center for Elements Strategy Initiative for Structural Materials, Kyoto University
  • Morikawa Tatsuya
    Department of Materials, Kyushu University

この論文をさがす

説明

<p>The temperature dependence of fatigue crack growth in stage IIb was investigated in Ti–0.49 mass%O with an alpha single phase. It was found that the fatigue crack growth rate in stage IIb was temperature independent at temperatures above 300 K. EBSD maps beside the fatigue crack showed that prismatic slips with ⟨a⟩ dislocations were dominantly activated during the fatigue crack growth. The reason why the prismatic slips were dominantly activated is discussed with numerical crystal plasticity analysis. It was shown that the local strain rate at the notch tip was higher than the macroscopic strain rate, which leads to the suppression of non-prismatic slips at the fatigue crack tip.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 63 (4), 600-606, 2022-04-01