温度および摩擦制御によるNi基超合金(Alloy720Li)の熱間均一圧縮試験

DOI Web Site Web Site 参考文献25件

書誌事項

タイトル別名
  • Uniform Hot Compression of Nickel-based Superalloy 720Li under Isothermal and Low Friction Conditions
  • オンド オヨビ マサツ セイギョ ニ ヨル Niキ チョウゴウキン(Alloy720Li)ノ ネツカン キンイツ アッシュク シケン

この論文をさがす

説明

<p>Isothermal compression tests at 1000°C and 0.1 s–1 strain rate, in which mica or glass sheets were used as a lubricant, were conducted. Isothermal condition was achieved by placing high-heat-resistant (HHR) alloys between a workpiece and ceramic tools in the induction-heating configuration to prevent heat from escaping to the ceramic tools. To perform high compression tests, it was necessary to increase the diameter of the HHR alloy, for which a new single-turn coil was designed using FEM calculation coupled with deformation-temperature electromagnetic fields. In order to obtain the correct flow stress, inverse analysis was conducted using the FEM calculation, in which temperature and strain rate fluctuations were compensated. However, the compensation was insufficient when the distribution of temperature and strain rate was large. The use of glass sheets as a lubricant considerably reduced friction and uniform deformation was achieved. Thus, flow stress obtained using the inverse analysis became extremely reliable. The flow stress of mica obtained using inverse analysis with a constant friction coefficient was different from that of glass. Introducing new friction model that the friction coefficient changed from 0.02 to 0.3, the flow stress of mica was consistent with that of glass. Therefore, the flow stress obtained using the inverse analysis for the new configuration proposed in this study proved to be reliable.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 108 (2), 107-119, 2022

    一般社団法人 日本鉄鋼協会

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ