Effect of Corrosion Products of Crack Face by Nitric Acid on Fatigue Crack Propagation Properties

DOI Web Site 8 References

Bibliographic Information

Other Title
  • 鋼材の疲労亀裂進展挙動に及ぼす硝酸による亀裂面腐食量の影響

Abstract

<p>Recently, multiple fatigue life extension techniques have been proposed utilizing crack closure, while no detailed mechanisms have been discussed for them. On the other hand, the authors have proposed the assessment method on crack initiation and propagation life based on an elasto-plastic model, and that would work for better assessment with detailed mechanisms of them. In this paper, fatigue crack growth tests were carried out using SENT specimens corroded at the crack length of 3mm by 35% HNO3, and shape measurements for fractured specimens were conducted after the tests. The results show that crack growth rates are retarded due to corrosion products between crack faces (Wedge effect). Furthermore, corrosion products distribute on the crack faces with 20 to 50µm thickness, which suggests correlations between the thickness of corrosion products and the level of life extension effect.</p>

Journal

References(8)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top