- Effect of Corrosion Products of Crack Face by Nitric Acid on Fatigue Crack Propagation Properties
抄録
<p>Recently, multiple fatigue life extension techniques have been proposed utilizing crack closure, while no detailed mechanisms have been discussed for them. On the other hand, the authors have proposed the assessment method on crack initiation and propagation life based on an elasto-plastic model, and that would work for better assessment with detailed mechanisms of them. In this paper, fatigue crack growth tests were carried out using SENT specimens corroded at the crack length of 3mm by 35% HNO3, and shape measurements for fractured specimens were conducted after the tests. The results show that crack growth rates are retarded due to corrosion products between crack faces (Wedge effect). Furthermore, corrosion products distribute on the crack faces with 20 to 50µm thickness, which suggests correlations between the thickness of corrosion products and the level of life extension effect.</p>
収録刊行物
-
- 材料
-
材料 72 (12), 873-878, 2023-12-15
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390861471537744896
-
- ISSN
- 18807488
- 05145163
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可