Effect of ZrO2 Addition on the Slag Corrosion Resistance of MgO-Al2O3 Spinel
-
- Fujita Motonari
- Okayama Ceramics Research Foundation
-
- Kita Hajime
- 岡山大学
-
- Igabo Koichi
- 岡山大学
-
- Sakida Shinichi
- 岡山大学
-
- Benino Yasuhiko
- 岡山大学
-
- Nanba Tokuro
- 岡山大学
-
- Miura Yoshinari
- 岡山大学
-
- Yamaguchi Akira
- Okayama Ceramics Research Foundation
Bibliographic Information
- Other Title
-
- MgO-Al2O3スピネルの耐スラグ侵食性におよぼすZrO2添加効果
- MgO Al2O3 スピネル ノ タイスラグ シンショクセイ ニ オヨボス ZrO2 テンカ コウカ
Search this article
Abstract
The changes in the microstructure and slag corrosion resistance of MgO-Al2O3 spinel due to the addition of ZrO2 were investigated. Densification due to ZrO2 addition was significant at the stoichiometric composition of the spinel(MgO=50mol%). Furthermore, the densification began at lower sintering temperatures along with the ZrO2 addition, which was confirmed in the sintered bodies containing2vol% of ZrO2. With increasing the relative density of the sintered bodies, the slag corrosion resistance was improved. In the specimens of2vol% ZrO2 addition, the slag corrosion resistance was higher than the ZrO2-free specimens with similar relative densities. In the case of 10 vol% ZrO2 addition, however, degradation in slag resistance was observed. It was finally concluded that the improvement in the slag resistance was resulted from the increase in slag viscosity originating in the elution of ZrO2 component.
Journal
-
- Taikabutsu
-
Taikabutsu 63 (6), 279-286, 2011-06-01
The Technical Association of Refractoreies,Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390018518956375040
-
- NII Article ID
- 10028225356
-
- NII Book ID
- AN00136247
-
- ISSN
- 27593835
- 00398993
-
- NDL BIB ID
- 11143033
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
-
- Abstract License Flag
- Disallowed